中文网站 | Call Us Today! +86-531-8803-2799|info@haihangchem.com
Home/Catalysts & Chemical Auxiliary Agents/Other/pOlybutadiene diacrylate cas 9003-17-2

pOlybutadiene diacrylate cas 9003-17-2

Chemicalname:POLYBUTADIENE DIACRYLATE

CAS No. 9003-17-2

Molecular Weight:54.09044

Appearance: White Powder

Category:

Description

POLYBUTADIENE DIACRYLATE Quick Details

Chemicalname:POLYBUTADIENE DIACRYLATE

CAS No. 9003-17-2

Molecular Weight:54.09044

Appearance: White Powder

POLYBUTADIENE DIACRYLATE Description and Usage

Performance

Butadiene rubber has high elasticity, low hysteresis loss and heat generation, low temperature, good fluidity in filling and in-mold, excellent wear resistance and flex resistance. However, the tensile strength is low, the wet skid resistance is poor, and the processing property is poor. The product is white or yellowish.

Use

BR9000 is a general-purpose non-oil-filled synthetic rubber that can be used in combination with natural rubber and other synthetic rubbers. Widely used in the manufacture of tires, hoses, tapes, seals, soles and other rubber products.

POLYBUTADIENE DIACRYLATE Specification

Specification Quality Standard
Superior grade First grade Qualified product
Volatility% ≤ 0.75 1.00 1.30
Total ash % ≤ 0.30 0.30 0.30
Raw rubber Mooney viscosity/ML(1 4)100℃ 45.0±5.0 45.0±5.0 45.0±7.0
Mixing rubber Mooney viscosity/ML(1 4)100℃ ≤ 68.0 70.0 73.0
300finite stress/MPa 25min35min50min 6.5—10.57.0—11.06.8—10.8 6.2—10.76.7—11.26.5—11.0 6.0—11.56.5—11.56.3—11.3
Tensile Strength/MPa35min≥ 14.2 13.7 13.2
Elongation5min ≥ 450 430 430
Anti-aging agent Non pollution Non pollution Non pollution
Quality Standard GB8659—88

POLYBUTADIENE DIACRYLATEPackage,ShippingandStorage

Packed in bags, the net weight of each bag is 25±0.5kg. The storage of the product requires normal temperature, ventilation, drying and cleaning. It should not be stored in the open air or in direct sunlight. During transportation, measures should be taken to prevent direct sunlight and rain. Transport carts should be cleaned to avoid damage to packaging and debris.